SHG Phase Matchable Range |
409.6-3500nm(Type I) |
525-3500nm(Type II) |
Therm Optic Coefficients(/℃) |
dno/dT=-9.3x 10-6/℃ |
|
|
dne/dT=-16.6x 10-6/℃ |
|
Absorption Coefficients |
<0.1%/cm at 1064nm <1%/cm at 532nm |
|
Angle Acceptance |
0.8mrad-cm (θ, Type I,1064 SHG) |
|
|
1.27mrad-cm (θ, Type II,1064 SHG |
|
Temperature Acceptance |
55℃-cm |
|
Spectral Acceptance |
1.1nm-cm |
|
Walk-off Angle |
2.7°(Type I 1064 SHG) |
|
|
3.2°(Type II 1064 SHG) |
|
NLO Coefficients |
deff (I)=d31sinθ+(d11cosΦ-d22sin3Φ)cosθ |
|
|
deff (II)=(d11sin3Φ+d22cos3Φ)cos2θ |
|
Non-vanished NLO susceptibilities |
d11=5.8xd36(KDP) |
|
|
d31=0.05xd11 |
|
|
d22<0.05xd11 |
|
sellmeier Equations(λ in μm ) |
no2=2.7359+0.01878 / (λ2-0.01822) -0.01354 λ2 |
|
|
ne2=2.3753+0.01224 / (λ2-0.01667) -0.01516 λ2 |
|
Electro-optic coefficients: |
r11=2.7pm/V, r22, r 31<0.1γ11 |
|
Half-wave voltage: |
7KV (at 1064nm,3*3*20mm3) |
|
Resistivity: |
>1011 ohm-cm |
|
Relative Dielectric Constant: |
εs11/εo:6.7 |
|
|
εs33/εo:8.1 |
|
|
Tan δ<0.001 |
|